Facile Approach in Development of Superhydrophobic-Superoleophilic Kaolin-Based Hollow Fibre Ceramic Membrane

Abstract

A silane coupling agent is an organosilicon compound with special structure possessing organic functional groups and hydrolysable groups. In this study, a superhydrophobic-superoleophilic nano-silica film on ceramic membrane was constructed by a modified Stöbertechnique by using tetraethoxy-silane (TEOS) and fluoroalkyl silane (FAS). The colloidal nano-silica based silane sol coating solution was synthesized via co-hydrolysis and co-condensation of TEOS and FAS. Particle size distribution of the colloidal nano-silica based silane sol was evaluated using particle size analyzer as depicted. The contents of the relative elements of the colloidal nano-silica based silane sol were examined using energy dispersive x-ray (EDX) spectra. Extent of superhydrophobicity-superoleophilicity was determined using the contact angle measurements. The surface wettability of superhydrophobicity-superoleophilicity was determined using the contact angle measurements. Also, the effects of grafting times and coating cycles on the wettability of the modified kaolin-based hollow fiber membrane were determined. The results revealed that the modified kaolin-based hollow fiber membrane exhibited oil contact of 0o and water contact angle of 160o and, demonstrating its considerable antiwetting applications like in oil-water filtration process. While, with an increase in grafting times and coating cycles, the wettability of the superhydrophobic-superoleophilic nano-silica film was enhanced due to increase in surface roughness provided by the hydrolysable groups on the surface of the ceramic membrane. In conclusion, this study presents a feasible route to the surface superhydrophobicity-superoleophilicity testing of ceramic membranes